Simultaneous adsorption-catalysis process for methylene blue removal using MOF-Fe/GNPs composites
DOI:
https://doi.org/10.51316/jca.2023.043Keywords:
GNPs, photocatalysis, dye wastewater treatmentAbstract
In this study, graphene nanoplatelets (GNPs) were combined with iron-organic framework materials using the ultrasonic method in a water/ethanol solvent. The resulting composite material had a clear crystalline morphology with a size range of 200 to 400 nm. The MOF-Fe particle grew in a particular order on GNPs, forming a uniform structure. The XRD diagram confirmed the presence of GNPs and MOF-Fe, with peaks at 21.103o and 26.728o assigned to GNPs, and peaks at 5.423o and 11.015o typical for MOF-Fe. The BET model estimated the surface area of MOF-Fe/GNPs at 441 m2/g. The composite showed high efficiency in treating chromogenic organic compounds through simultaneous adsorption and photocatalysis. Specifically, the material achieved over 80% methylene blue removal via adsorption mechanism after 2 hours, and 100% removal with simultaneous adsorption-photocatalysis treatment mechanism.
Downloads
References
N.H. Thuần, N.V. Giang, L.T.V. Anh, Tạp chí Khoa học và Công nghệ Việt Nam, 62(6) (2020) 52-57.
N.T. Dũng, Đ.T. Thêm, Đ.T. Oanh, N.T. Phượng, Tạp chí Phân tích Hóa, Lý và Sinh học, 22(4) (2017) 98-107.
L.T.X. Thùy, L.T. Sương, L.H. Thắng, L.T.B. Thảo, K. Oshita, Tạo chí Khoa học và Công nghệ, 22(11) (2017) 54-59.
H.N. Khánh, P.T. Hiếu, N.T.C. Tiên, V.T.T. Thùy, V.T. Hằng, N.N. Huy, Tạp chí Môi trường, 3(9) (2021) 83-87.
V.N. An, V.T.H. Hoa, L.V. Hiếu, Tạp chí Khoa học Đại học Đồng Tháp, 9(3) (2020) 41-51.
L.D.P. Nhung, T.T.B. Phượng, L.V. Tân, T. Thành, Tạp chí Tài nguyên và Môi trường, 1(4) (2021) 18-19.
B.X. Hiếu, T.N. Tuấn, L.H. Khoa, N.T.H. Phương, N.T.H. Phượng, Đ.T. Dũng, T.X. Tùng, T.V. Chinh, L.Đ. Dương, Tạp chí Xúc tác và Hấp phụ Việt Nam, 8(2) (2019) 57-61.
T.N. Tuấn, N.T. Thịnh, T.V. Chinh, L.Đ. Dương, N.T.H. Phượng, N.T.H. Phương, Tạp chí Xúc tác và Hấp phụ Việt Nam, 8(1) (2019) 110-114.
S. Norouzbahari, Z.M. Lighvan, A. Ghadimi, B. Sadatnia, Fuel, 339 (2023) 127463.
G. Lee, Md.A. Hossain, M. Yoon, S.H. Jhung, J Ind. and Eng. Chem., 119 (2023) 181-192. https://doi.org/10.1016/j.jiec.2022.12.005
E.V. Butyrskaya, Mat. To Com., 33 (2022) 104327. https://doi.org/10.1016/j.mtcomm.2022.104327
H.L. Hung, T. Iizuka, X. Deng, Q. Lyu, C.H. Hsu, N. Oe, L.C. Lin, N. Hosono, D.Y. Kang, Sep. and Pur. Tech., 310 (2023) 123115. https://doi.org/10.1016/j.seppur.2023.123115
J. Parikh, B. Mohan, K. Bhatt, N. Patel, S. Patel, A. Vyas, K. Modi, Mic. J., 184 (2023) 108156. https://doi.org/10.1016/j.microc.2022.108156
W. Niu, K. Kang, Y. Ou, Y. Ding, B. Du, X. Guo, Y. Tan, W. Hu, C. Gao, Y. He, Y. Guo, Sen. & Act.: B. Chemical, 381 (2023) 133347. https://doi.org/10.1016/j.snb.2023.133347
N.T.H. Phuong, L.T. Bac, N.D. Ha and L.D. Duong, ACS Omega, 6 (2021) 33419-33427. https://doi.org/10.1021/acsomega.1c03951
L.T. Bac, N.Q. Chau, N.T. Phuong, N.D. Ha, L.M. Tri, N.T.H. Phuong, L.D. Duong, ACS Omega, 7 (2022) 46674-46681. https://doi.org/10.1021/acsomega.2c05614
N.T.H. Phương, L.T.P. Thảo, N.B. Cường, Tạp chí Nghiên cứu Khoa học và Công nghệ quân sự, 9 (2020) 193-198.
N.Đ. Hà, N.Q. Châu, L.T. Bắc, N.T.H. Phương, Tạp chí Nghiên cứu Khoa học và Công nghệ quân sự, 12 (2022) 230-236. https://doi.org/10.54939/1859-1043.j.mst.FEE.2022.230-236.
L.T. Bac, N.T.H. Phuong, L.D. Duong, N.T. Phuong, Tạp chí Nghiên cứu Khoa học và Công nghệ quân sự, 76 (2021) 61-67. https://doi.org/10.54939/1859-1043.j.mst.76.2021.61-67.
N.T.H. Phuong, N.D. Ha, Viet J. Sci. Tech., 56 (3B) (2018) 219-227.
L.D. Duong, N.A. Tuan, N.T. Tung, N.D. Ha, N.T.H. Phuong, N.T. Tham, N.D. Anh, D.T. Dung, Eldon R. Rene, Soon Woong Chang, Hien Tran Thi, Dinh Duc Nguyen, Sustainability, 11 (2019) 7228. https://doi.org/10.3390/su11247228.
N.T.H. Phương, N.B. Quan, N.T. Phuong, N.B. Cuong, T.V. Chinh, J. Mil. Sci. Tech., 75A (2021) 17-28. https://doi.org/10.54939/1859-1043.j.mst.75A.2021.17-28.
Downloads
Published
Issue
Section
How to Cite